Re: Pre-bent brake lines--what do you know of gmoldtimeparts???

Posted by Tim Cole On 2013/7/22 18:21:31

Well, hopefully these stainless brake lines aren't too hard (lower chrome percentage). I'm not sure if stainless will anneal, but if it will I would anneal the flares to allow sealing at lower torque. Stainless 316 is about the same hardness as carbon steel (cold rolled), while 304 is significantly softer. I don't know what they use in brake lines, but it is definitely not high carbon.